17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ30MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ40MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ45MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ50MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ60MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ65MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ70MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ80MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ90MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ100MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ110MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ120MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ130MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ140MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ150MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ160MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ170MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ180MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ200MM 17CrNiMo6大型齒輪用鋼

17CrNiMo6滲碳合金結(jié)構(gòu)鋼|φ300MM 17CrNiMo6大型齒輪用鋼

======================

上海高高商貿(mào)有限公司：

聯(lián)系人：粟太成

地址：上海市寶山區(qū)撫遠路1288弄61號

==================================

17CrNiMo6是德國 DIN 17210-（86）標準的鋼號，歐標為18CrNiMo7-6,對應GB的 17Cr2Ni2Mo

17Cr2Ni2Mo不是GB材料，而是JB材料。具體的標準號為：JBT 6395-2010大型齒輪、齒圈鍛件.

化學成分

碳(C)：0.15-0.20,

硅(Si)：0.40,

錳(Mn)：0.40-0.60,

硫(S)：0.035,

磷(P)：0.035，

鉻(Cr)：1.50-1.80，

鎳(Ni)：1.40-1.70,

鉬(Mo)：0.25-0.35，

17CrNiMo6由于碳在鐵素體中的溶解度較?。s為0.025%），而在奧氏體狀態(tài)下，滲碳溫度越高，碳在其中的擴散系數(shù)越大，既滲碳速度越大。但溫度不宜過高，否則滲碳設備使用壽命顯著下降或損壞，而且溫度過高時間過長會造成滲層組織粗大，碳化物級別超差等缺陷。通常生產(chǎn)實際中采用900、930滲碳。

17CrNiMo6由于工件表面窮碳，接受活性碳原子的能力很強，滲碳速度較快，此時爐內(nèi)碳勢較低，需要向爐內(nèi)通過大量的滲劑，以維持爐內(nèi)的碳勢，具體還與裝爐量有關(guān)，此時如果不能及時補充滲劑，可能造成滲碳時間過長，碳濃度分布曲線下凹等缺陷，但也不能過強，否則可能出現(xiàn)大量網(wǎng)狀碳化物而無法消除。

17CrNiMo6滲碳合金結(jié)構(gòu)鋼以上由上海高高特鋼自行發(fā)行，如有對17CrNiMo6滲碳合金結(jié)構(gòu)鋼不詳之處，敬請來電洽談！高高特鋼將以真信息、真品質(zhì)、真價格的為您提供17CrNiMo6滲碳合金結(jié)構(gòu)鋼有關(guān)環(huán)節(jié)！